Autoria: |
BEZERRA, E. B.; FRANÇA, D. C.; MORAIS, D. D. de S. M.; ROSA, M. de F.; MORAIS, J. P. S.; ARAÚJO, E. M.; WELLEN, R. M. R. |
|
Afiliação: |
ELEIEBER BARROS BEEZERRA, UFCG; DANYELLE CAMPOS FRANÇA, UFCG; DAYANNE DINIZ de SOUZA MORAIS, UFCG; MORSYLEIDE DE FREITAS ROSA, CNPAT; JOAO PAULO SARAIVA MORAIS, CNPA; EDCLEIDE MARIA ARAÚJO, UFCG; RENATE MARIA RAMOS WELLEN, UFPB. |
|
Título: |
Processing and Properties of PCL/Cotton Linter Compounds. |
|
Ano de publicação: |
2017 |
|
Fonte/Imprenta: |
Materials Research, v. 20, n. 2, p. 317-325, 2017. |
|
DOI: |
10.1590/1980-5373-MR-2016-0084 |
|
Idioma: |
Inglês |
|
Conteúdo: |
Biodegradable compounds of poly(?-949;-caprolactone) (PCL)/ cotton linter were melting mixed with filling content ranging from 1% to 5% w/w. Cotton linter is an important byproduct of textile industry; in this work it was used in raw state and after acid hydrolysis. According to the results of torque rheometry no decaying of viscosity took place during compounding, evidencing absence of breaking down in molecular weight. The thermal stability increased by 20% as observed in HDT for PCL/cotton nanolinter compounds. Adding cotton linter to PCL didn't change its crystalline character as showed by XRD; however an increase in degree of crystallinity was observed by means of DSC. From mechanical tests in tension was observed an increase in ductility of PCL, and from mechanical tests in flexion an increase in elastic modulus upon addition of cotton linter, whereas impact strength presented lower values for PCL/cotton linter and PCL/cotton nanolinter compounds. SEM images showed that PCL presents plastic fracture and cotton linter has an interlacing fibril structure with high L/D ratio, which are in agreement with matrix/fibril morphology observed for PCL/cotton linter compounds. PCL/cotton linter compounds made in this work cost less than neat PCL matrix and presented improved properties making feasible its commercial use. |
|
Thesagro: |
Algodão. |
|
Thesaurus Nal: |
Cotton. |
|
Categoria do assunto: |
-- |
|
URL: |
https://ainfo.cnptia.embrapa.br/digital/bitstream/item/169872/1/Processing-and-properties.pdf
|
|
Marc: |
LEADER 01990naa a2200229 a 4500
001 2083626
005 2017-12-26
008 2017 bl uuuu u00u1 u #d
024 7 $a10.1590/1980-5373-MR-2016-0084$2DOI
100 1 $aBEZERRA, E. B.
245 $aProcessing and Properties of PCL/Cotton Linter Compounds.$h[electronic resource]
260 $c2017
520 $aBiodegradable compounds of poly(?-949;-caprolactone) (PCL)/ cotton linter were melting mixed with filling content ranging from 1% to 5% w/w. Cotton linter is an important byproduct of textile industry; in this work it was used in raw state and after acid hydrolysis. According to the results of torque rheometry no decaying of viscosity took place during compounding, evidencing absence of breaking down in molecular weight. The thermal stability increased by 20% as observed in HDT for PCL/cotton nanolinter compounds. Adding cotton linter to PCL didn't change its crystalline character as showed by XRD; however an increase in degree of crystallinity was observed by means of DSC. From mechanical tests in tension was observed an increase in ductility of PCL, and from mechanical tests in flexion an increase in elastic modulus upon addition of cotton linter, whereas impact strength presented lower values for PCL/cotton linter and PCL/cotton nanolinter compounds. SEM images showed that PCL presents plastic fracture and cotton linter has an interlacing fibril structure with high L/D ratio, which are in agreement with matrix/fibril morphology observed for PCL/cotton linter compounds. PCL/cotton linter compounds made in this work cost less than neat PCL matrix and presented improved properties making feasible its commercial use.
650 $aCotton
650 $aAlgodão
700 1 $aFRANÇA, D. C.
700 1 $aMORAIS, D. D. de S. M.
700 1 $aROSA, M. de F.
700 1 $aMORAIS, J. P. S.
700 1 $aARAÚJO, E. M.
700 1 $aWELLEN, R. M. R.
773 $tMaterials Research$gv. 20, n. 2, p. 317-325, 2017.
Download
Esconder MarcMostrar Marc Completo |
|
Registro original: |
Embrapa Algodão (CNPA) |
|
|
Biblioteca |
ID |
Origem |
Tipo/Formato |
Classificação |
Cutter |
Registro |
Volume |
Status |
URL |
Voltar
|
|
|
| Registros recuperados : 3 | |
| 1. |  | GOUVEIA, F. O.; COLLEVATTI, R. G.; TELLES, M. P. de C.; BORBA, T. C. de O.; SOARES, T. N. Estrutura genética espacial intrapopulacional em Annona crassiflora Mart. (Annonaceae). In: CONGRESSO DE PESQUISA, ENSINO E EXTENSÃO, 7., 2010, Goiânia. Conhecimento e desenvolvimento sustentável: anais... Goiânia: UFG, 2010. p. 5621-5625. Conpeex 2010.| Tipo: Artigo em Anais de Congresso |
| Biblioteca(s): Embrapa Arroz e Feijão. |
|    |
| 3. | | GOUVEIA, F. O.; RESENDE, L. V.; MELO, D. B.; BRONDANI, R. P. V.; CHAVES, L. J.; LIMA, J. S.; SANTANA, L. L.; TELLES, M. P. C.; SOARES, T. N. Isolamento e caracterização de marcadores microssatélites do genoma de Dipteryx alata Vogel. In: CONGRESSO BRASILEIRO DE GENÉTICA, 55., 2009, Águas de Lindóia, SP. Resumos... Ribeirão Preto: Sociedade Brasileira de Genética, 2009. p. 126.| Biblioteca(s): Embrapa Arroz e Feijão. |
| |
| Registros recuperados : 3 | |
|
| Nenhum registro encontrado para a expressão de busca informada. |
|
|